AlSi50粉末AlSi50 is an aluminum-silicon alloy powder containing 50% silicon and remainder aluminum. It offers an exceptional combination of properties like low density, high fluidity, low thermal expansion, high specific strength, and corrosion resistance. AlSi50 Powder Composition The typical composition of AlSi50 alloy powder is: Element Composition Aluminum (Al) Balance Silicon (Si) 48-52% Aluminum forms the matrix providing ductility, toughness and corrosion resistance. Silicon increases hardness, fluidity and reduces the coefficient of thermal expansion. The high 50% silicon content results in a eutectic composition with the lowest possible melting point and excellent castability. Strict control of the Al to Si ratio is critical. Properties of AlSi50 Powder AlSi50 powder possesses a… -
420 パウダー316Lはオーステナイト系ステンレス鋼である。17-4PHはマルテンサイト系析出硬化ステンレス鋼で、高強度、高硬度、高耐食性を有する。420はマルテンサイト系ステンレス鋼で、良好な機械的性質、熱伝導性、金型鋼に類似した研磨特性を有し、良好な耐食性を維持しています。物性 商標 サイズ範囲 サイズ分布 ホールフロー率 かさ密度 タップ密度 D10(Ã×m) D50(Ã×m) D90(Ã×m) 316L 15-53Ã×m 17-23 30-38 50-58 25s/50g 4.0g/cm3 4.5g/cm3 17-4PH 15-53Ã×m 4.0g/cm3 4.5g/cm3 420 15-53Ã×m 4.0g/cm3 4.5g/cm3 熱処理推奨事項 商標 熱処理推奨事項 316L 1050Í/2h/WQ 17-4PH 1040¡"C/2h +480¡"C/4h 420 1050¡"C/0.5h/WQ 機械的挙動 商標 硬度(HRC) 引張強さ(¿¼b/Mpa) 降伏... -
T15パウダーT15パウダーの概要 T15パウダーは、硬度、強度、靭性の優れた組み合わせを提供する炭化タングステン-コバルト超硬合金パウダーです。結合相として15%コバルトと共に炭化タングステンを高い割合で含んでいます。T15 粉末の主な特性と利点: T15 粉末の特性と特徴 特性詳細 組成 85% WC、15% Co 結合相 密度 13.0-14.5 g/cc 粒子形状 丸みを帯びた多面体 サイズ範囲 0.5-15 ミクロン 硬度 88-93 HRA (焼結時) 横断破壊強度 550-650 MPa コバルトマトリックスに保持された超硬タングステンカーバイド粒子により、T15 は産業、鉱業、建設部門における最も過酷な磨耗および摩耗条件に最適です。T15... -
GH4169パウダーGH4169パウダーは、熱処理後に高強度、高硬度、高耐食性を発揮するように設計された析出硬化ステンレス鋼パウダーです。17%クロムとニッケル、アルミニウム、チタン、ニオブを含有し、機械的特性と耐食性を向上させています。サイズ範囲 15-45um/15-53um/20-63um 45-105um 形状 球状 流動能力 ¨P25s 見掛密度 ¨4.0 g/cæØ 酸素含有量 ¨P200 ppm 窒素含有量 ¨P150ppm GH4169 粉末の主な特性：GH4169 粉末特性 特性詳細 組成 Fe-17Cr-4Ni-1.5Ti-0.7Al-0.25Nb 合金 密度 7.9g/cc 粒子形状 不規則、角型 サイズ範囲 10-150 ミクロン 見掛け密度 真密度の 50% まで 流動性 中程度 強度 時効処理後非常に高い 耐食性 海洋環境を含む優れた耐食性 GH4169 の卓越した強度対重量比... -
純銅粉Overview of Pure Copper Powder Pure copper powder contains 99.5% or higher copper content. It provides excellent thermal and electrical conductivity combined with good corrosion resistance, solderability, and bio-compatibility. Key properties and advantages of pure copper powder: Pure Copper Powder Properties and Characteristics Properties Details Composition 99.5% or higher copper content Density 8.94 g/cc Particle shape Spherical, irregular Size range 1-150 microns Apparent density Up to 50% of true density Conductivity Excellent, second only to silver Solderability Excellent due to oxidation resistance Bio-compatibility High, safe for food contact Pure copper powder is ideal for applications like welding products, brazing alloys, friction materials, diamond tools, electrical contacts, and metal injection molding…. -
Ti6Al4V パウダーTi6Al4V粉末の概要 Ti6Al4V粉末はグレード5チタン合金とも呼ばれ、最も人気のあるチタン合金粉末の一つです。6%のアルミニウムと4%のバナジウムを主要な合金元素として含み、残りはチタンです。球状粉末ti6al4vは、高強度、低重量、耐食性、生体適合性、加工性の優れた組み合わせを提供します。Ti6Al4V粉末の主な特性と利点: Ti6Al4V粉末の特性と特徴 特性の詳細 組成 Ti-6Al-4V 合金 密度 4.43 g/cc 粒子形状 主に球形 サイズ範囲 15-45 ミクロン 見かけ密度 真密度の最大60% 流動性 良好 チタン合金としては高強度 耐食性 優れている Ti6Al4Vは、航空宇宙、... -
アルミ合金系列Product Specification Apparent Density Flow Ability Oxygen Content Tensile Strength Yield Strength Elongation AISi10Mg 15-53Ã×m 45-105Ã×m 75-150Ã×m ¡Ô1.35g/cm3 ¨P80s/50g ¨P300ppm 300©I20Mpa 200©I20Mpa 20©I2% AMgScZr ¡Ô1.30g/cm3 ¨P80s/50g ¨P300ppm 545©I20Mpa 500©I20Mpa 10©I2% AK400 (can be anodized) ¡Ô1.30g/cm3 ¨P80s/50g ¨P300ppm 430©I20Mpa 300©I20Mpa 10©I2% Pure aluminum powder (purity 99.8%) ¡Ô1.20g/cm3 ¨P100s/50g ¨P1000ppm Process: Vacuum air atomization method Advantages: low satellite powder/hollow powder ratio, good fluidity, high sphericity, and high bulk density. Printed finished parts have high corrosion resistance, low density and mechanical strength High degree of heat treatment, requiring less heat treatment than castings Application: 3D printing lightweight, brackets and other structural parts, heat dissipation components, etc. in aerospace, automobile manufacturing and other industries… -
AlMgScZr粉末Overview of AlMgScZr Powder AlMgScZr powder is an aluminum alloy containing magnesium, scandium and zirconium as the main alloying elements. It exhibits excellent strength, weldability and corrosion resistance while maintaining the low density advantage of aluminum. Key properties and advantages of AlMgScZr powder include: AlMgScZr Powder Properties and Characteristics Properties Details Composition Al-Mg-Sc-Zr alloy Density 2.7 g/cc Particle shape Spherical Size range 10-75 microns Apparent density Up to 60% of true density Flowability Excellent Strength Very high for Al alloy powder Weldability Excellent AlMgScZr powder enables fabrication of lightweight structural and functional components across aerospace, automotive, and industrial sectors needing high specific strength. AlMgScZr Powder Composition Typical composition of AlMgScZr… -
純粋なアルミニウム粉末 (Junsui na aruminiumu funmatsu)Overview of Pure Aluminum Powder Pure aluminum powder contains 99% or higher aluminum content. It provides low density combined with good ductility, conductivity, and corrosion resistance. Key properties and advantages of pure aluminum powder include: Pure Aluminum Powder Properties and Characteristics Properties Details Composition 99% or higher Al content Density 2.7 g/cc Particle shape Spherical, irregular Size range 1-150 microns Apparent density Up to 50% of true density Conductivity Excellent electrical and thermal conductivity Corrosion resistance Good due to protective oxide layer Pure aluminum powder is suitable for applications like thermite welding, diamond tools, conductive coatings, pyrotechnics, and metal injection molding. Pure Aluminum Powder Composition Typical composition of pure aluminum… -
高温合金系列製品仕様 見かけ密度 フロー能力 酸素含有量 引張強さ 降伏強さ 伸び GH3625 15-53Ã×m 45-105Ã×m 75-150Ã×m Ô4.40g/cm3 ¨P20s/50g ¨P300ppm 1000©I50Mpa 600©I50Mpa 35©I5% GH4169 Ô4.20g/cm3 ¨P20s/50g ¨P300ppm 1250©I30Mpa 1000©I30Mpa 18©I3% GH3230 ¡Ô4.40g/cm3 ¨P20s/50g ¨P300ppm 930©I30Mpa 930©I30Mpa 25©I5% GH3536 ¨4.40g/cm3 ¨P20s/50g ¨P300ppm 850©I30Mpa 550©I20Mpa 42©I5% プロセス：真空空気噴霧法 利点：真球度が高く、サテライトパウダーが小さく、流動性がよく、かさ密度が高い。印刷された製品は、良好な耐疲労性、耐酸化性能、構造安定性を有する 用途：航空宇宙および工業用タービンディスク、リング、ブレード、機械およびその他の構造、航空宇宙エンジン燃焼室 包装：アルミ箔袋/プラスチックボトル/鉄ドラムなどの通常の包装、真空包装または不活性ガス充填包装など。