AlMgScZr粉末Overview of AlMgScZr Powder AlMgScZr powder is an aluminum alloy containing magnesium, scandium and zirconium as the main alloying elements. It exhibits excellent strength, weldability and corrosion resistance while maintaining the low density advantage of aluminum. Key properties and advantages of AlMgScZr powder include: AlMgScZr Powder Properties and Characteristics Properties Details Composition Al-Mg-Sc-Zr alloy Density 2.7 g/cc Particle shape Spherical Size range 10-75 microns Apparent density Up to 60% of true density Flowability Excellent Strength Very high for Al alloy powder Weldability Excellent AlMgScZr powder enables fabrication of lightweight structural and functional components across aerospace, automotive, and industrial sectors needing high specific strength. AlMgScZr Powder Composition Typical composition of AlMgScZr… -
純粋なアルミニウム粉末 (Junsui na aruminiumu funmatsu)Overview of Pure Aluminum Powder Pure aluminum powder contains 99% or higher aluminum content. It provides low density combined with good ductility, conductivity, and corrosion resistance. Key properties and advantages of pure aluminum powder include: Pure Aluminum Powder Properties and Characteristics Properties Details Composition 99% or higher Al content Density 2.7 g/cc Particle shape Spherical, irregular Size range 1-150 microns Apparent density Up to 50% of true density Conductivity Excellent electrical and thermal conductivity Corrosion resistance Good due to protective oxide layer Pure aluminum powder is suitable for applications like thermite welding, diamond tools, conductive coatings, pyrotechnics, and metal injection molding. Pure Aluminum Powder Composition Typical composition of pure aluminum… -
高温合金系列製品仕様 見かけ密度 フロー能力 酸素含有量 引張強さ 降伏強さ 伸び GH3625 15-53Ã×m 45-105Ã×m 75-150Ã×m Ô4.40g/cm3 ¨P20s/50g ¨P300ppm 1000©I50Mpa 600©I50Mpa 35©I5% GH4169 Ô4.20g/cm3 ¨P20s/50g ¨P300ppm 1250©I30Mpa 1000©I30Mpa 18©I3% GH3230 ¡Ô4.40g/cm3 ¨P20s/50g ¨P300ppm 930©I30Mpa 930©I30Mpa 25©I5% GH3536 ¨4.40g/cm3 ¨P20s/50g ¨P300ppm 850©I30Mpa 550©I20Mpa 42©I5% プロセス：真空空気噴霧法 利点：真球度が高く、サテライトパウダーが小さく、流動性がよく、かさ密度が高い。印刷された製品は、良好な耐疲労性、耐酸化性能、構造安定性を有する 用途：航空宇宙および工業用タービンディスク、リング、ブレード、機械およびその他の構造、航空宇宙エンジン燃焼室 包装：アルミ箔袋/プラスチックボトル/鉄ドラムなどの通常の包装、真空包装または不活性ガス充填包装など。 -
GH 3625 粉末GH3625粉末の概要 GH3625粉末は、25%クロムを含有し、モリブデンとアルミニウムを添加した時効硬化性ニッケル鉄基合金です。高温での高強度、高硬度、耐食性、耐酸化性という優れた特性を兼ね備えています。GH3625 粉末の主な特性と利点は以下の通りです：GH3625 粉末の特性と特徴 特性詳細 組成 Ni-25Cr-4.5Mo-3.5Al 合金 密度 8.2g/cc 粒子形状 主に球形 サイズ範囲 15-45 ミクロン 見かけ密度 真密度の 60% まで 流動性 良好 時効処理後の強度 非常に高い 耐食性 孔食や隙間腐食を含む優れた耐食性 GH3625 は、高い耐食性を必要とする航空宇宙、石油・ガス、化学処理、発電分野で広く使用されています。 -
Cu 99.95 粉末Cu 99.95パウダーの概要 Cu 99.95パウダーは、電解タフピッチ（ETP）銅粉とも呼ばれ、99.95%以上の銅を含む高純度銅粉です。優れた電気伝導性と熱伝導性を持ち、機械的特性も優れています。主な用途は、電気接点、ブラシ、溶接製品、ろう付け、摩擦材、ダイヤモンド工具などです。Cu 99.95パウダーの主な特性と利点は以下の通りです：Cu 99.95パウダーの特性と特徴 特性の詳細 組成 最低銅量99.95% 密度 8.94 g/cc 粒子形状 不規則、角型 サイズ範囲 2-150ミクロン 見掛け密度 真密度の最大50% 流動性 低～中程度 導電性 優れた電気および熱伝導性 焼結性 良好... -
CuSn10 パウダーOverview of CuSn10 Powder CuSn10 powder is a copper-tin alloy containing approximately 10% tin and the remainder copper. It offers an excellent combination of strength, ductility, corrosion resistance, wear resistance, and antifriction properties. Key properties and applications of CuSn10 powder include: CuSn10 Powder Properties and Characteristics Properties Details Composition 90% copper, 10% tin Density 8.8 g/cc Particle shape Irregular, angular Size range 5-150 microns Apparent density Up to 50% of true density Flowability Moderate Strength Excellent for Cu alloy powder Ductility Good Corrosion resistance Very good CuSn10 is widely used in bearing cages, bushings, welding rods, and wear parts across the automotive, electrical, and industrial sectors. CuSn10 Powder Composition Typical… -
銅合金シリーズ製品仕様 見掛密度 流動性 酸素含有量 引張強さ 降伏強さ 伸び CuCrZr 15-53μm 45-105μm 75-150μm Ô4.10g/cm3 ¨P30s/50g ¨P600ppm 350©I35Mpa 175©I10Mpa 8©I2% CuZn40 ¡4.25g/cm3 ¨P30s/50g ¨P600ppm CuSn10 ¡4.10g/cm3 ¨P30s/50g ¨P600ppm プロセス：真空空気噴霧法 利点印刷製品は熱伝導性、電気伝導性に優れ、設計と組み合わせることで、複雑な内部構造や冷却流路を持つ製品部品を製造することができる：航空宇宙エンジンのスラストチャンバーなどの部品、冷却効果の高い3Dプリント金型製品など。包装アルミホイル袋/プラスチックボトル/鉄製ドラム缶などの通常包装、真空包装、不活性ガス充填包装など。 -
銅ベースはんだProduct description Copper solder paste is prepared by a special process from copper-based brazing powder, trace active components, solvents, polymer carriers and other additives. Grades and specifications Model Product Type Composition(wt%) Powder Size(M) Brazing temperature(¡Í) Brazing method YTCu-1 Paste Cu:93:P:7 -200 -235 743-840 Furance, flame, resistance, High frequency brazing YTCu-2 Paste Cu:92.5;P:7.5 -200 -235 730-830 YTCu-3 Paste Cu:86;P:7;Sn:7 -200 -235 700-750 YTCu-4 Paste Cu:75;Sn;P;Ni, etc. -200 -235 600-650 9414 Powder Cu:88;Ni:5;Sn:7 -200 -235 890-900 1. Suitable for flame welding, resistance welding, high frequency welding and furnace welding between various copper and copper alloys. 2. Solder paste can be applied manually to the area to be soldered, and can also be… -
CuCrZr 粉末CuCrZr粉末の概要 CuCrZr粉末は、銅（Cu）、クロム（Cr）、ジルコニウム（Zr）から成る合金粉末です。CuCrZr粉末は、高強度、良好な導電性、高温での耐軟化性を必要とする高性能用途に適した、ユニークな特性の組み合わせを提供します。CuCrZr粉末の組成 CuCrZrは析出硬化型合金であり、その高強度は金属マトリックス中に形成されたコヒーレントな析出物からもたらされる。組成は、最適な析出硬化反応を達成する上で重要な役割を果たします。以下に代表的な組成範囲を示す：銅 (Cu) 残部 クロム (Cr) 0.5 - 1.2 wt% ジルコニウム (Zr) 0.03 - 0.3 wt% 銅はマトリックスを形成し、... -
430L 粉末430Lパウダーの概要 430Lパウダーは17%クロムを含有するフェライト系ステンレス鋼パウダーで、耐食性を向上させるためにモリブデンとニオブを添加しています。耐食性、強度、溶接性、コストの最適なバランスを提供します。430Lパウダーの主な特性と利点: 430Lパウダーの特性と特徴 特性詳細 組成 Fe-17Cr-Nb-Mo 合金 密度 7.7 g/cc 粒子形状 不規則、角型 サイズ範囲 10-150ミクロン 見かけ密度 真密度の50%まで 流動性 中程度 耐食性 多くの環境で優れている 強化 固溶体および析出強化 430Lパウダーは、化学処理、船舶用ハードウェア、自動車排気部品、工業用バルブおよびフランジ、耐候性を必要とする構造部品などに広く使用されています。