アルミ合金系列
Product Specification Apparent Density Flow Ability Oxygen Content Tensile Strength Yield Strength Elongation AISi10Mg 15-53Ã×m 45-105Ã×m 75-150Ã×m ¡Ô1.35g/cm3 ¨P80s/50g ¨P300ppm 300©I20Mpa 200©I20Mpa 20©I2% AMgScZr ¡Ô1.30g/cm3 ¨P80s/50g ¨P300ppm 545©I20Mpa 500©I20Mpa 10©I2% AK400 (can be anodized) ¡Ô1.30g/cm3 ¨P80s/50g ¨P300ppm 430©I20Mpa 300©I20Mpa 10©I2% Pure aluminum powder (purity 99.8%) ¡Ô1.20g/cm3 ¨P100s/50g ¨P1000ppm Process: Vacuum air atomization method Advantages: low satellite powder/hollow powder ratio, good fluidity, high sphericity, and high bulk density. Printed finished parts have high corrosion resistance, low density and mechanical strength High degree of heat treatment, requiring less heat treatment than castings Application: 3D printing lightweight, brackets and other structural parts, heat dissipation components, etc. in aerospace, automobile manufacturing and other industries…
小さなMOQ
何百もの製品に柔軟に対応
カスタマイズ・サポート
産業に応じてカスタマイズされたパウダー
迅速な出荷
DHLエクスプレスで、安全かつ迅速にお客様のお手元にお届けします。
製品 | 仕様 | 見掛け比重 | 流動性 | 酸素含量 | 引張強度 | 降伏強度 | 伸長 |
AISi10Mg |
15~53×m
45~105mm 75×150~150×300ミクロン |
¡Ô1.35g/cm3 | ¨P80s / 50g | ¨P300ppm | 300©I20Mpa | 200MPa(200©I) | 20©I2% |
AMgScZr | 1.30g/cm3 | ¨P80s / 50g | ¨P300ppm | 545©I20Mpa | 500©I20Mpa | 10©I2% | |
AK400 (アルマイト可能です) | 1.30g/cm3 | ¨P80s / 50g | ¨P300ppm | 430©I20Mpa | 300©I20Mpa | 10©I2% | |
純アルミニウム粉末(純度99.8%) | 1.20g/cm3 | ¨P100s/50g | ¨P1000ppm |
プロセス:真空中気体アトマイゼーション法
利点: 低いサテライトパウダー/ホロパウダー比率、良好な流動性、高い球形度と高いバルク密度。印刷完成品は高い耐腐食性、低密度および機械的強度を有する
高温処理の度合いが高く、鋳物よりも低い処理温度で必要十分な硬度が得られる
アプリケーション: 3Dプリント軽量化、航空宇宙・自動車製造などにおけるブラケットやその他構造部品、放熱部品など